Semiconductor device and method of fabrication thereof

ABSTRACT

A semiconductor device and a method of fabricating such a semiconductor device in which a silicon nitride film constituting a protective film for ion implantation is used for improving the device structure in order that conversion of a metal film into a silicide for reducing the resistance of a shallow-junction diffused layer may not be prevented by the knock-on phenomenon of oxygen, thereby reduce the fabrication cost. A silicon nitride film, which is used as a protective film for ion implantation into a substrate and a gate polysilicon, is processed into side walls of the gate polysilicon thereby to omit the step of forming side walls by a silicon oxide film. Further, in the case where boron is diffused into the gate polysilicon, boron diffusion is suppressed by nitrogen knock-on, thereby preventing boron from going through the gate oxide film.

This application is a Divisional of U.S. patent application Ser. No. 08/580,460, filed Dec. 27, 1995, now U.S. Pat. No. 5,648,673

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device and to a method of fabrication thereof, and more in particularly to a method of fabricating a semiconductor device having a metal silicide film on a conductor or a diffused layer.

2. Description of the Related Art

To improve the degree of integration of LSI, it is necessary to reduce the depth of the junction of the impurities diffused layer in the source/drain regions. A reduced thickness of the diffused layer, however, increases the resistance value of the diffused layer and results in a reduced operating speed of the semiconductor. In view of this, semiconductor devices have conventionally been fabricated by the method described below.

First, device isolation regions are formed on a P-type silicon substrate, and a plurality of gate electrodes, each including a gate oxide film and a polycrystal silicon, are sequentially formed on the substrate. A small amount of N-type impurities are injected into the substrate, and a silicon oxide film is formed over the entire surface of the substrate. This silicon oxide film is anisotropically etched, thereby forming sidewall oxide films on the side walls of each gate electrode. Further, ion implantation of N-type impurities into the substrate with high energy forms a MOSFET of LDD (lightly doped drain) structure. After that, a metal film is formed over the entire surface of the substrate, and a metal silicide film is formed on each of the impurity diffused layers and the gate electrodes by heat treatment. The portion of the metal film that has not been converted into a silicide is then removed. These steps fabricate a MOSFET with the source/drain resistance reduced by the metal silicide film.

In carrying out ion implantation into the silicon substrate, a silicon oxide film is formed as a protective film on the substrate surface to prevent the substrate surface from roughening and the implant profile defect due to the channeling, and ions are implanted through this silicon oxide film. Ion implantation through an oxide film, however, results in introduction of oxygen into the silicon substrate due to the bombardment of the implanted ions and develops a phenomenon called "knock-on". The proportion of oxygen thus knocked on increases when impurities large in mass such as arsenic are implanted. When a metal silicide layer is formed on the impurity diffused layer formed by ion implantation, the knock-on phenomenon causes the oxygen introduced into the silicon substrate to suppress the formation of a silicide. As a result the thickness of the metal silicide layer is reduced to such an extent that it is difficult to reduce the resistance of the source/drain regions This problem is especially conspicuous with the N-type impurity diffused layer subjected to ion-implantation of arsenic.

In manufacture of a P-type MOSFET by the above-mentioned fabrication methods boron may be implanted as impurities into a polysilicon film constituting a gate electrode. Since the diffusion coefficient of boron is high, however, boron in the gate electrode is diffused into the channel region of the substrate through the gate oxide film thereby causing variations in the threshold voltage of the MOSFET

JP-A-64-760 discloses a fabrication method in which oxygen ions are not introduced into the silicon substrate and the silicon substrate surface is thus prevented from becoming rough. More specifically, after sidewall oxide films are formed, a silicon nitride film is formed over the entire surface of the substrate, and impurities are implanted into the substrate with high energy through the silicon nitride film, thereby forming an impurity diffused layer. In this method, nitrogen, not oxygen, is introduced into the silicon substrate and the gate electrodes by knock-on, and therefore conversion into silicide is not suppressed.

This method, however, requires the additional steps of forming a silicon nitride film over the entire surface of a silicon substrate after forming sidewall oxide films on the side walls of each gate electrode by anisotropic etching of a silicon oxide film, and also removal of the silicon nitride film used as a protective film by using hot phosphoric acid after implanting impurities with high energy. Thus the fabrication steps of a semiconductor device become complicated. The same semiconductor device is fabricated in large quantities at a time, and therefore, a change in even a single fabrication step has a great effect on the production cost and poses a very serious problem.

SUMMARY OF THE INVENTION

Accordingly, an object of the present invention is to provide a semiconductor device and a method of fabrication thereof in which a sufficiently thick metal silicide layer having a low resistance is formed on impurity diffused layers or electrodes without complicating the fabrication steps of a semiconductor device as described above. Another object of the invention is to provide a semiconductor device and a method of fabrication thereof in which the boron diffused in the electrodes is reduced.

According to a first aspect of the invention, there is provided a semiconductor device comprising a semiconductor substrate, an insulating film patterned on the semiconductor substrate, a conductor patterned on the insulating film, an impurity diffused layer containing nitrogen and impurity and formed at least in the portions of the semiconductor substrate on both sides of the conductor, a sidewall insulating film containing a nitride film and formed on side walls of the conductor, and a metal silicide film formed at least on the impurity diffused layer.

Also, according to the first aspect of the invention, there is also provided a method of fabricating a semiconductor device, which comprises the steps of forming a first insulating film on a semiconductor substrate and patterning a conductor on the first insulating film; forming a second insulating film including a nitride film over the entire surface of the semiconductor substrate formed with the first insulating film and the conductor and then implanting impurity ions into the semiconductor substrate at least on both sides of the conductor through the second insulating film while at the same time introducing the nitrogen of the nitride film into the semiconductor substrate on the both sides of the conductor; etching the second insulating film and thereby forming a sidewall insulating film including the second insulating film on each side wall of the conductor to expose the portion of the semiconductor substrate outside of the sidewall insulating film; and forming a metal silicide film on the portion of the semiconductor substrate at least outside the sidewall insulating film.

According to a second aspect of the invention, there is provided a semiconductor device comprising a semiconductor substrate, an insulating film patterned on the semiconductor substrate, a conductor containing nitrogen and formed as a pattern on the insulating film, a sidewall insulating film including a nitride film formed on the side walls of the conductor, and a metal silicide film formed at least on the conductor.

Also, according to the second aspect of the invention, there is also provided a method of fabricating a semiconductor device, which comprises the step of forming a first insulating film on a semiconductor substrate and patterning a conductor on the first insulating film; forming a second insulating film including a nitride film over the entire surface of the semiconductor substrate formed with the first insulating film and the conductor and implanting impurity ions into the conductor through the second insulation film while at the same time introducing the nitrogen of the nitride film into the conductor; etching the second insulating film and forming a sidewall insulating film including the second insulating film on the side walls of the conductor, and forming a metal silicide film at least on the conductor.

According to a third aspect of the invention, a method for fabricating a semiconductor device, comprises the steps of forming an insulating film on a semiconductor substrate and a conductor on the insulating film and then patterning the conductor, implanting at least boron and nitrogen into the conductor, and forming a metal silicide film at least on the conductor.

The first or second aspect of the invention provides a relatively simple semiconductor device and a simple method of fabricating the semiconductor device in which conversion to a silicide of the impurity diffused layer or the conductor is not suppressed using a nitride film as a protective film for ion implantation and using a part of the nitride film as a side wall of the conductor. According to the second or third aspect of the invention, on the other hand, there is provided a relatively simple semiconductor device and a simple method of fabricating the semiconductor device in which conversion of the conductor into a silicide is not suppressed and boron diffusion into the conductor is reduced in the case where boron is implanted as an impurity for reducing the resistance of polysilicon used as the conductor.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A to 1H are sectional views showing a semiconductor device and the sequence of steps for fabricating it according to a first embodiment of the invention;

FIGS. 2A to 2H are sectional views showing a semiconductor device and the sequence of steps for fabricating it according to a second embodiment of the invention;

FIGS. 3A to 3D are sectional views showing a semiconductor device and the sequence of steps for fabricating it according to a third embodiment of the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

A first embodiment of the invention applied to a CMOS device will be explained below with reference to FIGS. 1A to 1H.

First, as shown in FIG. 1A, an N-well 102 and a P-well 103 are formed on a P-type silicon substrate 101, and a field oxide film 104 is formed by, for example, the local oxidation of silicon (LOCOS) method.

Then, as shown in FIG. 1B, a silicon oxide film 105 having about 5 to 20 nm thickness is formed on each of the N-well 102 and the P-well 103 by the thermal oxidation method, after which a non-doped polycrystal silicon film 106, 100 to 300 nm thick, is deposited by the chemical vapor deposition (CVD) method on the silicon oxide film. N-type impurities are ion-implanted into the polycrystal silicon films 106, and after a heat treatment to reduce the resistance of the polycrystal silicon film 106, a patterning is effected by the photolithography technique. Thus forming a gate polysilicon film 106 is formed made up of the polycrystal silicon film 106 on each of the N-well 102 and the P-well 103 respectively. Also, the silicon oxide film 105 is removed except for the portion thereof directly under each gate polysilicon film 106.

In the next step, as shown in FIG. 1C, with the N-well 102 masked by a photoresist 107, phosphorus is ion-implanted in the P-well 103 in a dosage of 2×10¹³ /cm² with an energy of 40 keV, followed by heat treatment to form the N⁻ source/drain regions 108 of the NMOSFET.

As shown in FIG. 1D, the photoresist 107 is removed, and the P-well 103 is masked by a photoresist 110. Under this condition, the N-well 103 is ion-implanted by boron in a dosage of 2×10¹³ /cm³ with an energy of 15 keV in the N-well 102, so that P⁻ source/drain regions 109 of a PMOSFET are formed by heat treatment.

In the next step, as shown in FIG. 1E, the photoresist 110 is removed, and a silicon nitride film 111, about 100 to 300 nm thick, is formed over the entire surface of the substrate by the CVD process. In the case where the substrate surface is already oxidized naturally or similarly otherwise, the silicon nitride film 111 is formed on an oxide film. Since the oxide film is relatively thin as compared with the silicon nitride film 111, however, conversion of titanium into a silicide described later is not greatly affected. Next, with the N-well 102 masked with a photoresist 112, the P-well 103 is ion-implanted with arsenic in a dosage of about 5×10¹⁴ to 1×10¹⁶ /cm² with an energy of 30 to 100 keV. In the process, arsenic ions are implanted into the P-well 103 through the silicon nitride film 111. Then, N⁻ source/drain regions 113 of an NMOSFET are formed by heat treatment.

As the next step, as shown in FIG. 1F, the photoresist 112 is removed, and the P-well 103 is masked by a photoresist 114. Under this condition, the N-well 102 is ion-implanted with BF2 in a dosage of 1×10¹⁴ to 5×10¹⁶ /cm² with an energy of 20 to 90 keV, followed by heat treatment for forming P⁺ source/drain regions 115 of a PMOSFET. Also in this process, BF₂ is ion-implanted into the N-well 102 through the silicon nitride film 111.

As shown in FIG. 1G, the photoresist 114 is removed, after which the silicon nitride film 111 is etched off by anisotropic etching except for the portion thereof on the side walls of each of side walls of the gate polysilicon film 106. As a result, sidewall insulating film 111 made of the silicon nitride film 111 is formed on each of side walls of the gate polysilicon film 106. After that, a titanium film 116 having the thickness of about 40 nm is deposited over the entire surface by sputtering.

Then, as shown in FIG. 1H, the substrate 101 is heat-treated for about 5 to 60 seconds at the temperature of 400 to 900° C. to form titanium silicide films 117 by self-alignment only on the gate polysilicon films 106 and the diffused layers 113 and 115. The titanium film 116 remaining without being converted into silicide and the reaction products other than silicide are removed by a mixture solution of ammonium, hydrogen peroxide and water or by a solution containing fluoric acid. Consequently, the titanium film 116 on the sidewall insulating film 111 is removed, so that the gate polysilicon film 106 and the titanium silicide films 117 on the sides thereof are insulatively isolated from each other.

As shown in FIG. 1H, a layer insulating film 118 is formed over the entire surface, and a plurality of contact holes 119 are formed in the layer insulating film 118 to form aluminum (Al) wiring layers 120.

According to the fabrication method described above, a silicon nitride film 111 is used as a protective film in forming the impurities diffused layer 113 of the N-well 102 and the impurities diffused layer 115 of the P-well 103. Therefore, the roughening of the substrate surface by ion implantation and the implantation profile defect which otherwise might be caused by channeling can be prevented, while at the same time introducing nitrogen but not oxygen into the substrate by "knock-on". Thus, conversion of the titanium into a silicide is not suppressed. Hence, a titanium silicide film 117 having sufficient thickness can be obtained on each diffused layer 113, 115, with the result that each MOSFET, even with a small junction depth of the source/drain regions, can have reduced resistance, thereby preventing decrease in operating speed of each device.

The nitrogen concentration in these impurity diffused layers 113 and 115 is preferably 10¹⁸ to 10²¹ cm³.

Further, since the silicon nitride film 111 used as a protective film for ion implantation is anisotropically etched to provide sidewall insulating films of the gate polysilicon film 106, the sidewall insulating films of a silicon oxide film is not required to be formed separately unlike in the prior art. The number of fabrication step, therefore, need not be increased.

According to the first embodiment, a P-type well and an N-type well are formed on a silicon substrate to apply the invention to a CMOS device. In applications to usual MOS devices, however, a field oxide film and a silicon oxide film providing a gate oxide film are formed directly on a silicon substrate.

Also, although the N⁻ region 108 and the P⁻ region 109 are formed in the source and drain of a NMOSFET and PMOSFET respectively to produce an LDD structure in the embodiment described above, these regions may be omitted in the case where lateral diffusion of impurities due to heat treatment after ion implantation is a problem.

Further, according to the above embodiment, heat treatment is carried out after each of the ion implantation for forming the impurity diffused layer 113 and the ion implanation for forming the impurity diffused layer 115 to activate the impurities. Alternatively, heat treatment may be omitted for activating the impurities immediately after the ion implantation for forming the impurity diffused layer 113. Instead, N₂ annealing may be carried out at the temperature of, for example, 850° C. for 30 minutes to activate the impurities of the impurity diffused layers 113 and 115 at the same time after the ion implantation for forming the impurity difused layer 115.

Furthermore, according to the above embodiment, in forming the gate polysilicon film 106, the non-doped polycrystal silicon film is formed over the entire surface and is ion-implanted with N-type impurities to reduce the resistance thereof, after which a gate-electrode pattern is formed. As an alternative to this method, phosphorus diffusion may be used instead of ion implantation of N-type impurities. Further, the polycrystal silicon film may be patterned into gate electrodes, and when forming the impurity diffused layers 113, 115 of the wells 102, 103, impurity ions of respective conduction type may be implanted simultaneously into the gate polysilicon film 106 through the silicon nitride film 111 to reduce the resistance of the gate polysilicon film 106. In such a case, the silicon nitride film 111 functions as a protective film at the time of ion implantation into each gate silicon film 106, and nitrogen is introduced into each gate polysilicon film 106 by knock-on. Conversion into a silicide, therefore, is not suppressed when a titanium silicide film 117 is subsequently formed on the gate polysilicon film 106. Thus, the titanium silicide film 117 thus having sufficient thickness is formed on the gate polysilicon film 106 to reduce the resistance of the gate electrodes.

The nitrogen concentration in this gate polysilicon film (gate electrode) 106 is preferably 10¹⁸ to 10²¹ /cm³.

In forming the titanium silicide film 117, heat treatment may be carried out for 5 to 60 seconds at 600 to 1100° C. after removal of the remaining titanium film, thereby further reducing the resistance of the titanium silicide film 117. Further, a metal for forming a silicide may be molybdenum (M), tungsten (W), tantalum (Ta) or cobalt (Co) or a similar high melting point metal in place of titanium (Ti).

Generally, since boron has high diffusion coefficient, if used for forming a P-type impurity diffused layer in a silicon substrate, boron diffuses deeply into the substrate by heat treatment after ion implantation, with the result that it is difficult to produce a shallow junction. In the case where the silicon nitride film 111 is used as a protective film for ion implantation as in the above embodiment, however, nitrogen introduced into the substrate by knock-on suppresses the diffusion of boron, and therefore a shallow junction can be easily formed even if baron is used as an impurity.

The second embodiment of the invention represents an application to a device having a field shield electrode. With the recent increase in the degree of integration of semiconductor devices, the field shield isolation method is closely watched in place of the LOCOS method. The field shield isolation method is such that the voltage potential of each field shield electrode formed through a field shield insulating film in a device isolation region is set as a fixed voltage thereby to isolate devices. The second embodiment will be described with reference to FIGS. 2A to 2H.

First, as shown in FIG. 2A, a silicon oxide film 202 is formed by thermal oxidation on a silicon substrate 201, and a non-doped polycrystal silicon film is formed thereon by the CVD method. This polycrystal silicon film is selectively etched for patterning field shield electrodes 203.

Then, as shown in FIG. 2B, a silicon oxide film 204 is formed over the entire surface of the substrate by the CVD method.

As the next step, as shown in FIG. 2C, the silicon oxide films 202 and 204 are selectively removed by the anisotropic etching according to the RIE process in a manner such as to leave the silicon oxide film 204 only on the side walls of the field shield electrodes 203. In this way, sidewall oxide films 204 are formed on the side walls of each field shield electrode 203.

As shown in FIG. 2D, a silicon oxide film 205 is formed by thermal oxidation on the silicon substrate 201. In the process, a thermal oxidation film is formed also on the uppermost surface of the shield electrodes 203. A non-doped polycrystal silicon film 206 is formed by the CVD method over the entire surface of the substrate, after which as shown in FIG. 2E, the silicon oxide film and the polycrystal silicon film are selectively etched by the RIE or a similar method, thereby forming gate oxide films 205 and gate electrodes 206 The thermal oxidation film on the uppermost surface of the shield electrodes 203 is, at the same time, also removed by etching.

Then, as shown in FIG. 2F, a silicon nitride film 207 is formed at the thickness of about 100 to 300 nm by the CVD method over the entire surface of the substrate, and impurities ions are implanted into the silicon substrate 201, the field shield electrodes 203 and the gate electrodes 206 through the silicon nitride film 207. Thus, impurity diffused layers 208 are formed in the substrate while at the same time reducing the resistance of the field shield electrodes and the gate electrodes.

As shown in FIG. 2G, the silicon nitride films are selectively removed by anisotropic etching by the RIE method or the like, so that sidewall nitride films 207 are formed only on the side walls of the field shield electrodes 203 and the gate electrodes 206.

As shown in FIG. 2H, a titanium film having the thickness of about 40 nm is deposited on the entire surface of the substrate by sputtering, and then a titanium silicide film 209 is formed by self-alignment only on each of the impurity diffused layers 208, the field shield electrodes 203 and the gate electrodes 206 by the heat treatment conducted for 5 to 60 seconds at the temperature of 400 to 900° C. The titanium film not converted into a silicide and the reaction products other than the silicide are cleaned off. Further, a layer insulating film 210 is formed over the entire surface of the substrate, and contact holes 211 are formed on the layer insulating film 210 to form aluminum wiring layers 212.

In the fabrication method described above, the silicon nitride films 207 function as a protective film when impurity ions are implanted into the field shield electrodes 203, so that nitrogen is introduced into the field shield electrodes 203 by knock-on. Conversion into a silicide, therefore, is not subsequently suppressed when the titanium silicide film 209 is formed on the field shield electrodes 203. Hence, the titanium silicide film 209 of a sufficient thickness is formed on the field shield electrodes 203, the gate electrodes 206 and the impurity diffused layers 208 to reduce the resistance of these component elements.

The second embodiment may use boron for forming an impurities diffused layer, in which case the nitrogen introduced into the substrate by knock-on suppresses boron diffusion, and therefore the threshold voltage variations of the MOS transistor is decreased, thereby facilitating the forming of a shallow junction in the impurity diffusion layer.

This effect of suppressing boron diffusion is attained when nitrogen is injected directly into electrodes or the source/drain regions as well as when impurities are injected into electrodes or the source/drain regions through a nitride film. More specifically, in FIG. 2F, a similar effect is achieved by injecting boron and nitrogen directly into the silicon substrate 201, the field shield electrodes 203 and the gate electrodes 206 without forming the silicon nitride film 207, and by forming a metal silicide film on the silicon substrate 201, the field shield electrodes 203 and the gate electrodes 206 as shown in FIG. 2H while omitting the process of forming the sidewall nitride films 207 shown in FIG. 2G.

Now, a third embodiment of the invention applied to the wiring in a semiconductor device will be explained with reference to FIGS. 3A to 3D. According to this embodiment, a semiconductor device comprises a plurality of memory cells, each including a MOS transistor and a capacitor, and a peripheral circuit for driving the memory cells.

In FIG. 3A, reference numeral 301 designates a semiconductor substrate comprising a memory cell forming region A (left) and a peripheral circuit forming region B (right) with a device isolation region 302 inbetween. A gate oxide film 303, a gate electrode 304, sidewall insulating films 305 and impurity diffused layers 306 are formed on the left side of the semiconductor substrate 301 according to the method described in the first or second embodiment. These elements make up one of a plurality of MOS transistors arranged in matrix. In a similar fashion, a gate oxide film 323, a gate electrode 324, a sidewall insulating film 325 and impurity diffused layers 326 are formed on the right side of the semiconductor substrate 301. These elements make up one of a plurality of MOS transistors of the peripheral circuit. These two types of MOS transistors are preferably formed concurrently formed.

As shown in FIG. 3B, insulating films 307 and 327 are patterned on gate electrodes 304 and 324 respectively, after which a polycrystal silicon film containing impurities and constituting a lower electrode 308 of a capacitor, a dielectric film 309 and a polycrystal silicon film containing impurities and constituting an upper electrode 310 of the capacitor are sequentially formed by patterning. The lower electrode 308 of the capacitor is connected to one of the impurity diffused layers 306 of a corresponding MOS transistor in the memory cell region. After that, an insulating film 311 of BPSG (boron phosphor silicon glass) or the like is formed over the entire surface of the substrate, and contact holes 312, 313, 332, 333 are opened in the insulating film 311. Further, this step is followed by patterning a wiring (bit wire) 314 for connecting the other impurity diffused layer 306 of the MOS transistor in the memory cell region to one of the impurity diffused layers 326 of the MOS transistor in the peripheral circuit forming region and patterning a on-doped polycrystal silicon providing wirings 315 and 335.

Then, as shown in FIG. 3C, a silicon nitride film 316 about 100 to 300 nm in thickness is formed over the entire surface of the substrate by the CVD method, after which impurities are implanted into the wiring layer through the silicon nitride film 316 to reduce the resistance of the wiring layer. In the process, nitrogen in the silicon nitride film 316 is also knocked on to the wiring layer. In the case where boron is used as an impurity implanted into the wiring layer, nitrogen injected into the substrate by knock-on suppresses boron diffusion in the wiring layer. It is therefore easy to form a shallow junction in the impurity diffused layers 306 and 326. Further, the insulating layer 316 is formed over the entire surface of the substrate, and a wiring 334 is connected, for example, to a power source voltage (V_(DD)) and a wiring 314 to a voltage of V_(DD) /2 through contact holes (not shown) formed in the insulating film 316. Alternatively, boron and nitrogen may be implanted into the wiring layer directly without forming the silicon nitride film 316.

As the next step, as shown in FIG. 3D, the silicon nitride film is selectively removed and a side-wall nitride film 316 is formed only on each side wall of the wirings 314, 315, 335. This process is omitted when the silicon nitride film 316 is not formed. Furthermore, a titanium film is deposited to the thickness of about 40 nm by sputtering over the entire surface of the substrate, after which the substrate is heat treated for 5 to 60 seconds at the temperature of 400 to 900° C. Titanium silicide films 317 are thus formed by self-alignment only on the wirings 314, 315 and 335. As a result, the wirings 314, 315 and 335 can be reduced in resistance. The titanium film left without being converted into a silicide and the reaction products other than silicide are cleaned off. In addition, a layer insulating film 318 is formed over the entire surface of the substrate, and the wiring 335 is connected to the power source voltage (V_(DD)) and the wiring 315 to a voltage of V_(DD) /2 through the contact holes (not shown) in the layer insulating film 318.

As described above, according to this invention, a semiconductor device comprising a metal silicide layer of sufficient thickness capable of forming a low-resistance shallow junction can be fabricated with a comparatively small number of steps for a reduced fabrication cost. Also, variations in the threshold voltage of the MOS transistor can be suppressed by suppressing the boron diffusion into a conductor even when boron is used as an impurity. 

What is claimed is:
 1. A method of fabricating a semiconductor device, comprising the steps of:forming a gate insulating film on a semiconductor substrate and forming a gate electrode on said gate insulating film; forming a silicon nitride film over said semiconductor substrate formed with said gate insulating film and said gate electrode; implanting ions of an impurity into at least a first region of said semiconductor substrate on both sides of said gate electrode through said silicon nitride film and introducing nitrogen of said nitride film into at least the first region of said semiconductor substrate; etching said silicon nitride film to form a sidewall insulating film on sidewalls of said gate electrode; and exposing said semiconductor substrate in a second region where neither said gate electrode nor said sidewall insulating film is formed, forming a metal film over said semiconductor substrate formed with said gate insulating film, said gate electrode and said sidewall insulating film, and subjecting said semiconductor substrate to heat treatment to form a metal silicide film on at least the second region of said semiconductor substrate.
 2. A method of fabricating a semiconductor device according to claim 1, wherein said second region of said semiconductor substrate is a source/drain region.
 3. A method of fabricating a semiconductor device according to claim 1, further comprising the step of:removing a portion of said metal film that has not been converted into said silicide film.
 4. A method of fabricating a semiconductor device according to claim 1, wherein said implantation step includes implanting ions of an impurity into the first region of said semiconductor substrate and said gate electrode through said nitride film and introducing nitrogen of said nitride film into the first region of said semiconductor substrate and said gate electrode.
 5. A method of fabricating a semiconductor device, comprising the steps of:forming a first well including an impurity of a first conductive type and a second well including an impurity of a second conductive type in a semiconductor substrate; forming a first gate insulating film on said first well and a second gate insulating film on said second well and forming a first gate electrode on said first gate insulating film and a second gate electrode on said second gate insulating film; forming a silicon nitride film over said first and second wells formed with said first and second gate insulating films and said first and second gate electrodes, respectively; implanting ions of an impurity of the second type into at least a first region of said first well on both sides of said first gate electrode through said silicon nitride film and introducing nitrogen of said silicon nitride film into at least the first region of said first well; implanting ions of an impurity of the first type into at least a second region of said second well on both sides of said second gate electrode through said silicon nitride film and introducing nitrogen of said silicon nitride film into at least the second region of said second well; etching said silicon nitride film to form sidewall insulating films on sidewalls of said first and second gate electrodes; and exposing said first well in a third region where neither said first gate electrode nor said sidewall insulating film is formed and exposing said second well in a fourth region where neither said second gate electrode nor said sidewall insulating film is formed, forming a metal film over said first and second wells formed with said first and second gate insulating films, said first and second gate electrodes and said sidewall insulating films, respectively, and subjecting said semiconductor substrate to heat treatment to form metal silicide film on at least the third region of said first well and the fourth region of said second well.
 6. A method of fabricating a semiconductor device according to claim 5 wherein said third region of said first well and said fourth region of said second well are source/drain regions.
 7. A method of fabricating a semiconductor device according to claim 5, further comprising the step of:removing a portion of said metal film that has not been converted into said silicide film.
 8. A method of fabricating a semiconductor device according to claim 5, wherein:said step of implanting ions of a second impurity type includes implanting ions of an impurity of the second conductive type into the first region of said first well and said first gate electrode through said silicon nitride film and introducing nitrogen of said nitride film into the first region of said first well and said first gate electrode; and said step of implanting ions of a first impurity type includes implanting ions of an impurity of the first conductive type into the second region of said second well and said second gate electrode through said silicon nitride film and introducing nitrogen of said silicon nitride film into the second region of said second well and said second gate electrode.
 9. A method of fabricating a semiconductor device according to claim 5, wherein the first conductive type is a selected one of N type and P type, and the second conductive type is the other of N type and P type.
 10. A method of fabricating a semiconductor device, comprising the steps of:pattern forming an insulating film on a semiconductor substrate and forming a conductor on said insulating film; forming a nitride film over said semiconductor substrate formed with said insulating film and said conductor; implanting ions of an impurity into at least said conductor through said nitride film and introducing nitrogen of said nitride film into at least said conductor; etching said nitride film to form a sidewall insulating film on sidewalls of said conductor; and forming a metal silicide film on at least said conductor after said nitride film is formed.
 11. A method of fabricating a semiconductor device comprising, the steps of:pattern forming an insulating film on a semiconductor substrate and forming a conductor on said insulating film; forming a silicon nitride film over said semiconductor substrate formed with said insulating film and said conductor; implanting ions of an impurity into at least a first region of said semiconductor substrate on both sides of said conductor through said silicon nitride film and introducing nitrogen of said silicon nitride film into at least the first region of said semiconductor substrate; etching said silicon nitride film to form a sidewall insulating film on sidewalls of said conductor; and exposing said semiconductor substrate in a second region where neither said conductor nor said sidewall insulating film is formed, and forming a metal silicide film on at least the second region of said semiconductor substrate.
 12. A method of fabricating a semiconductor device according to claim 11 wherein said implantation step includes implanting ions of an impurity into the first region of said semiconductor substrate and said conductor through said silicon nitride film and introducing nitrogen of said silicon nitride film into the first region of said semiconductor substrate and said conductor.
 13. A method of fabricating a semiconductor device according to claim 10 wherein said conductor is a field shield electrode.
 14. A method of fabricating a semiconductor device according to claim 11 wherein said conductor is a field shield electrode.
 15. A method of fabricating a semiconductor device according to claim 10, wherein said conductor is used for wiring within said semiconductor device.
 16. A method of fabricating a semiconductor device according to claim 10, wherein:said semiconductor device comprises a plurality of memory cells each having a MOS transistor and a capacitor; and said conductor is used for wiring for selecting a part of said memory cells.
 17. A method of fabricating a semiconductor device according to claim 1, wherein thickness of said silicon nitride film is about 100 to 300 nm.
 18. A method of fabricating a semiconductor device according to claim 5, wherein thickness of said silicon nitride film is about 100 to 300 nm.
 19. A method of fabricating a semiconductor device according to claim 10 wherein thickness of said silicon nitride film is about 100 to 300 nm.
 20. A method of fabricating a semiconductor device according to claim 11, wherein thickness of said silicon nitride film is about 100 to 300 nm.
 21. A method of fabricating a semiconductor device according to claim 1, wherein said semiconductor substrate is a silicon substrate.
 22. A method of fabricating a semiconductor device according to claim 5 wherein said semiconductor substrate is a silicon substrate.
 23. A method of fabricating a semiconductor device according to claim 10 wherein said semiconductor substrate is a silicon substrate.
 24. A method of fabricating a semiconductor device according to claim 11 wherein said semiconductor substrate is a silicon substrate and said nitride film is a silicon nitride film.
 25. A method of fabricating a semiconductor device according to claim 1, wherein the first region of said semiconductor substrate, into which ions of an impurity are implanted includes nitrogen of about 10¹⁸ to 10²¹ /CM³.
 26. A method of fabricating a semiconductor device according to claim 5 wherein the first and second regions, into which ions of an impurity is implanted includes nitrogen of about 10¹⁸ to 10²¹ /CM³.
 27. A method of fabricating a semiconductor device according to claim 10 wherein said conductor, into which ions of an impurity are implanted, includes nitrogen of about 10¹⁸ to 10²¹ /CM³.
 28. A method of fabricating a semiconductor device according to claim 11, wherein the first region of said semiconductor substrate, into which ions of an impurity are implanted, includes nitrogen of about 10¹⁸ to 10²¹ /CM³.
 29. A method of fabricating a semiconductor device according to claim 2, wherein the heat treatment in said heating step is carried out for about 5 to 60 seconds at a temperature of about 400° to 900° C.
 30. A method of fabricating a semiconductor device according to claim 6, wherein the heat treatment in said heating step is carried out for about 5 to 60 seconds at a temperature of about 400° to 900° C.
 31. A method of fabricating a semiconductor device according to claim 2, wherein said metal film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 32. A method of fabricating a semiconductor device according to claim 6, wherein said metal film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 33. A method of fabricating a semiconductor device according to claim 10 wherein said metal film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 34. A method of fabricating a semiconductor device according to claim 11 wherein said metal silicide film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 35. A method of fabricating a semiconductor device, comprising the steps of:(a) forming a silicon nitride film on a silicon semiconductor substrate; (b) implanting impurity ions of a p-type into a desired region of said silicon semiconductor substrate thereby introducing nitrogen atoms and silicon atoms of said silicon nitride film as well as said impurity ions into a surface layer of said silicon semiconductor substrate; (c) removing said silicon nitride film; (d) forming a metal film on said silicon semiconductor substrate; and (e) subjecting said silicon semiconductor substrate with said metal film formed thereon to heat treatment to change said metal film into a metal silicide film including said nitrogen atoms.
 36. A method according to claim 35, further comprising, prior to said step a), the step of:implanting impurity ions of a p-type into a predetermined region of said silicon semiconductor substrate.
 37. A method according to claim 35, wherein said metal film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 38. A method according to claim 35, further comprising, prior to step c), the step of:subjecting said silicon semiconductor substrate to heat treatment thereby activating impurity ions included in said surface layer of said silicon semiconductor substrate to form impurity diffusion layers.
 39. A method according to claim 35, wherein said steps c) and d) are performed under a condition that there is substantially no oxygen.
 40. A method of fabricating a semiconductor device, comprising the steps of:a) forming a silicon nitride film on a silicon semiconductor substrate in which a device isolation region is formed, a first well of a first conductive type and a second well of a second conductive type are formed in surface layers of said silicon semiconductor substrate respectively, a first insulating film and a second insulating film are formed on said first and second wells respectively, and a first pattern film and a second pattern film are formed on said first and second insulating films respectively, said second conductive type being opposite to said first conductive type; b) masking a first region of said silicon semiconductor substrate, in which said first well is formed, by using a first photo-resist mask and implanting impurity ions of the first conductive type into said silicon semiconductor substrate thereby introducing nitrogen atoms and silicon atoms of said silicon nitride film as well as said first impurity ions into a surface layer of said second well; c) removing said first photo-resist mask; d) masking a second region of said silicon semiconductor substrate, in which said second well is formed, by using a second photo resist mask and implanting impurity ions of the second conductive type into said silicon semiconductor substrate thereby introducing nitrogen atoms and silicon atoms of said silicon nitride film as well as said impurity ions of the second conductive type into a surface layer of said first well; e) removing said second photo resist mask; f) removing said silicon nitride film so that said silicon nitride film remains at least on sidewalls of said first and second pattern films; g) forming a metal film on said silicon semiconductor substrate; h) subjecting said silicon semiconductor substrate with said metal film formed thereon to heat treatment thereby changing said metal film into a metal silicide film including said nitrogen atoms; and i) removing said metal film which is not changed into said metal silicide film.
 41. A method according to claim 40, wherein said step a) includes forming a silicon nitride film on a silicon semiconductor substrate in which non-doped silicon films are formed as said first and second pattern films.
 42. A method according to claim 41, wherein each of said steps b) and d) includes implanting impurity ions into said non-doped silicon films.
 43. A method according to claim 40, wherein said metal film includes one selected from titanium, molybdenum, tungsten, tantalum and cobalt.
 44. A method according to claim 40, further comprising, after said step d), the steps of:subjecting said silicon semiconductor substrate to heat treatment thereby activating impurity ions included in said surface layer of said silicon semiconductor substrate to form impurity diffusion layers.
 45. A method according to claim 40, further comprising, after said step f), the steps of:subjecting said silicon semiconductor substrate to heat treatment thereby activating impurity ions included in said surface layer of said silicon semiconductor substrate to form impurity diffusion layers.
 46. A method according to claim 40, wherein:said impurity ions of the first conductive type includes donor type impurity ions; and said impurity ions of the second conductive type includes accepter type impurity ions.
 47. A method according to claim 46, wherein said step b) includes implanting said impurity ions in a dosage of from about 5×10¹⁴ to about 1×10¹⁶ /cm² with energy of from about 30 to about 100 keV.
 48. A method according to claim 46, wherein said step d) includes implanting said impurity ions in a dosage of from about 1×10¹⁴ to about 5×10¹⁶ /cm² with energy of from about 20 to about 90 keV. 